高韧性 Ultramid® PA66 德国巴斯夫 8202HS 低粘度 耐化学 用于薄壁部件 家具 把手
Ultramid® 8202 HS
Polyamide 6
BASF Corporation
产品说明：
Ultramid 8202 HS is a heat stabilized, low viscosity, general purpose PA6 injection molding. It possesses the combination of strength and toughness and has excellent chemical and abrasion resistance. The heat stabilizer system extends the retention of properties at the more elevated temperatures. Excellent in filling thin walls or areas.
Applications
Ultramid 8202 HS is generally recommended for drapery hardware, gears, fittings, furniture casters, bearings, handles, clips, fasteners and thin parts.
物性信息：
| 添加剂 | 热稳定剂 |
| 特性 | 低粘度 均聚物 良好的强度 良好耐磨损性 耐化学性良好 热稳定性 韧性良好 通用 |
| 用途 | 把手 薄壁部件 齿轮 家具 紧固件 配件 轴承 |
| 机构评级 | EC 1907/2006 (REACH) |
| RoHS 合规性 | RoHS 合规 |
| 形式 | 粒子 |
| 加工方法 | 注射成型 |
| 多点数据 | Isothermal Stress vs. Strain (ISO 11403-1) Secant Modulus vs. Strain (ISO 11403-1) Shear Modulus vs. Temperature (ISO 11403-1) Viscosity vs. Shear Rate (ISO 11403-2) |
| 比重 | 1.13 | -- | g/cm³ | ASTM D792, ISO 1183 |
| 收缩率 - 流动 (3.18 mm) | 1.2 | -- | % | |
| 吸水率 | ||||
| 24 hr | 1.6 | -- | % | ASTM D570 |
| 23°C, 24 hr | 1.6 | -- | % | ISO 62 |
| 饱和 | 9.5 | -- | % | ASTM D570 |
| 饱和, 23°C | 9.5 | -- | % | ISO 62 |
| 平衡, 50% RH | 2.7 | -- | % | ASTM D570 |
| 平衡, 23°C, 50% RH | 2.7 | -- | % | ISO 62 |
| 洛氏硬度 (R 级) | 119 | -- | ASTM D785 |
| 拉伸模量 | ISO 527-2 | |||
| 23°C | 2700 | 970 | MPa | ISO 527-2 |
| 80°C | 485 | 550 | MPa | ISO 527-2 |
| 121°C | 360 | 320 | MPa | ISO 527-2 |
| 抗张强度 | ||||
| 屈服, -40°C | 126 | 110 | MPa | ASTM D638, ISO 527-2 |
| 屈服, 23°C | 79.0 | 36.0 | MPa | ASTM D638 |
| 屈服, 80°C | 35.0 | 30.0 | MPa | ASTM D638, ISO 527-2 |
| 屈服, 121°C | 25.0 | 20.0 | MPa | ASTM D638, ISO 527-2 |
| 屈服, 23°C | 78.0 | 36.0 | MPa | ISO 527-2 |
| 断裂, 23°C | 75.0 | 60.0 | MPa | ASTM D638 |
| 伸长率 | ||||
| 屈服, 23°C | 4.0 | 16 | % | ASTM D638, ISO 527-2 |
| 屈服, 80°C | 42 | 35 | % | ASTM D638 |
| 屈服, 121°C | 36 | 40 | % | ASTM D638 |
| 断裂, 23°C | 55 | > 100 | % | ASTM D638 |
| 标称拉伸断裂应变 (23°C) | 25 | > 50 | % | ISO 527-2 |
| -40°C | 3010 | 3660 | MPa | ASTM D790 |
| 23°C | 2830 | 740 | MPa | ASTM D790 |
| 65°C | 500 | -- | MPa | ASTM D790 |
| 90°C | 350 | -- | MPa | ASTM D790 |
| 121°C | 305 | -- | MPa | ASTM D790 |
| 23°C | 2400 | 770 | MPa | ISO 178 |
| 弯曲强度 | ||||
| -40°C | 170 | 154 | MPa | ASTM D790 |
| 23°C | 108 | 35.0 | MPa | ASTM D790 |
| 65°C | 30.0 | -- | MPa | ASTM D790 |
| 90°C | 20.0 | -- | MPa | ASTM D790 |
| 121°C | 17.0 | -- | MPa | ASTM D790 |
| 23°C | 85.0 | 25.0 | MPa | ISO 178 |
| 简支梁缺口冲击强度 (23°C) | 3.5 | -- | kJ/m² | ISO 179 |
| 简支梁无缺口冲击强度 | ISO 179 | |||
| -30°C | 51 | -- | kJ/m² | ISO 179 |
| 23°C | 无断裂 | -- | ISO 179 | |
| 悬壁梁缺口冲击强度 | ASTM D256 | |||
| -40°C | 48 | 43 | J/m | ASTM D256 |
| 23°C | 58 J/m | 无断裂 | ASTM D256 | |
| Drop Impact Resistance (23°C) | 142 | > 271 | J | 内部方法 |
| 载荷下热变形温度 | ||||
| 0.45 MPa, 未退火 | 178 | -- | °C | ASTM D648 |
| 1.8 MPa, 未退火 | 65.0 | -- | °C | ASTM D648 |
| 1.8 MPa, 未退火 | 60.0 | -- | °C | ISO 75-2/A |
| 熔融峰值温度 | 220 | -- | °C | ASTM D3418, ISO 3146 |
| 线形热膨胀系数 - 流动 | 8.3E-5 | -- | cm/cm/°C | ASTM E831 |
| RTI Elec | UL 746 | |||
| 0.710 mm | 130 | -- | °C | UL 746 |
| 1.50 mm | 130 | -- | °C | UL 746 |
| 3.00 mm | 130 | -- | °C | UL 746 |
| 6.00 mm | 130 | -- | °C | UL 746 |
| RTI Imp | UL 746 | |||
| 0.710 mm | 95.0 | -- | °C | UL 746 |
| 1.50 mm | 105 | -- | °C | UL 746 |
| 3.00 mm | 105 | -- | °C | UL 746 |
| 6.00 mm | 105 | -- | °C | UL 746 |
| RTI | UL 746 | |||
| 0.710 mm | 95.0 | -- | °C | UL 746 |
| 1.50 mm | 105 | -- | °C | UL 746 |
| 3.00 mm | 105 | -- | °C | UL 746 |
| 6.00 mm | 105 | -- | °C | UL 746 |
| 体积电阻率 | ||||
| 1.50 mm | > 1.0E+13 | -- | ohms·cm | ASTM D257 |
| -- | > 1.0E+13 | -- | ohms·cm | IEC 60093 |
| 介电强度 | ||||
| 1.50 mm 1 | 22 | -- | kV/mm | ASTM D149 |
| -- | 37 | -- | kV/mm | IEC 60243-1 |
| 漏电起痕指数 | 600 | -- | V | IEC 60112 |
高韧性 Ultramid® PA66 德国巴斯夫 8202HS 低粘度 耐化学 用于薄壁部件 家具 把手
德国巴斯夫pa66,8202HS,耐化学PA66,低粘度 pa66,聚酰胺