高流动 美国奥升德 PA66 R530HR BK652 耐疲劳 增强级 抗冻 汽车发动机零件

手机版链接：https://m.trustexporter.com/cz12543481.htm
高流动 美国奥升德 PA66 R530HR BK652 耐疲劳 增强级 抗冻 汽车发动机零件 Vydyne® R530HR BK652Polyamide 66Ascend Performance Materials Operations LLC30% 玻璃纤维增强材料产品说明：Vydyne R530HR is specifically formulated to give superior hydrolysis resistance for demanding automotive cooling system components. This product has demonstrated more than twice the tensile strength and elongation retention of standard 30% glass-fiber reinforced PA66 after 3,500 hours of aging in automotive coolant at 120° C. Vydyne R530HR demonstrates similar property retention benefits at 130° C for 1,000 hours of coolant aging as well.Typical Applications/End Uses:To come物性信息：基本信息填料/增强材料玻璃纤维增强材料, 30% 填料按重量添加剂热稳定剂润滑剂特性抗冻抗溶剂性流动性高耐化学性良好耐疲劳性能耐汽油性热稳定性润滑用途汽车的发动机罩下的零件机构评级ASTM D 4066 PA0121G30ASTM D 6779 PA0121G30UL文件号E70062外观黑色形式粒子加工方法注射成型物理性能干燥调节后的单位制测试方法密度1.37--g/cm³ISO 1183收缩率ISO 294-4     垂直流动方向 : 23°C, 2.00 mm0.90--%ISO 294-4     流动方向 : 23°C, 2.00 mm0.40--%ISO 294-4吸水率ISO 62     23°C, 24 hr0.90--%ISO 62     平衡, 50% RH1.9--%ISO 62机械性能干燥调节后的单位制测试方法拉伸模量 (23°C)96507100MPaISO 527-2拉伸应力 (断裂, 23°C)185145MPaISO 527-2拉伸应变 (断裂, 23°C)4.05.0%ISO 527-2弯曲模量 (23°C)90005500MPaISO 178弯曲应力 (23°C)270190MPaISO 178Poisson's Ratio (23°C)0.40--ISO 527冲击性能干燥调节后的单位制测试方法简支梁缺口冲击强度ISO 179     -30°C1011kJ/m²ISO 179     23°C1116kJ/m²ISO 179简支梁无缺口冲击强度ISO 179     -30°C87110kJ/m²ISO 179     23°C95110kJ/m²ISO 179悬壁梁缺口冲击强度ISO 180     -30°C1011kJ/m²ISO 180     23°C1213kJ/m²ISO 180热性能干燥调节后的单位制测试方法热变形温度     0.45 MPa, 未退火258--°CISO 75-2/B     1.8 MPa, 未退火247--°CISO 75-2/A熔融温度260--°CISO 11357-3线形热膨胀系数ISO 11359-2     流动 : 23 到 55°C, 2.00 mm2.2E-5--cm/cm/°CISO 11359-2     横向 : 23 到 55°C, 2.00 mm1.1E-4--cm/cm/°CISO 11359-2高流动 美国奥升德 PA66 R530HR BK652 耐疲劳 增强级 抗冻 汽车发动机零件 美国奥升德 PA66,R530HR BK652,高流动pa66,抗冻性PA66,增强级pa66