物性表
拉伸强度 | ASTM D638 | 90.0 | Mpa | |
弯曲模量 | ASTM D790 | 3660 | Mpa | |
断裂点伸长率 | ASTM D638 | 6.0 | % | |
缺口冲击强度 | ASTM D256 | 140 | J/m | |
非缺口冲击强度 | ASTM D256 | 960 | J/m | |
热变形温度 | 66 psi, 未退火 | ASTM D648 | 250 | °C |
线性热膨胀系数 | 平行流动方向 | ASTM E831 | 0.000050 | cm/cm/℃ |
熔点 | DSC | 263 | °C | |
UL阻燃等级 | UL 94 | HB |
![PA66-广告20 PA66-广告20](http://cn.trustexporter.com/skin/default/image/lazy.gif)
拉伸强度 | ASTM D638 | 90.0 | Mpa | |
弯曲模量 | ASTM D790 | 3660 | Mpa | |
断裂点伸长率 | ASTM D638 | 6.0 | % | |
缺口冲击强度 | ASTM D256 | 140 | J/m | |
非缺口冲击强度 | ASTM D256 | 960 | J/m | |
热变形温度 | 66 psi, 未退火 | ASTM D648 | 250 | °C |
线性热膨胀系数 | 平行流动方向 | ASTM E831 | 0.000050 | cm/cm/℃ |
熔点 | DSC | 263 | °C | |
UL阻燃等级 | UL 94 | HB |