熔体质量流动速率 | 300°C/5.0kg | ASTMD1238 | 17 | g/10min |
熔体体积流动速率 | 300°C/5.0kg | ISO1133 | 16.4 | cm3/10min |
收缩率 | MD:3.20mm | 内部方法 | 0.20to0.50 | % |
吸水率 | 24hr | ASTMD570 | 0.060 | % |
室外适用性 | UL746C | f1 |
拉伸模量2 | ASTMD638 | 4350 | Mpa | |
拉伸模量 | ISO527-2/1 | 4400 | Mpa | |
抗张强度3 | 断裂 | ASTMD638 | 63.0 | Mpa |
拉伸应力 | 断裂 | ISO527-2 | 64.0 | Mpa |
伸长率 | 断裂 | ASTMD638 | 3.0 | % |
拉伸应变 | 断裂 | ISO527-2 | 3.0 | % |
弯曲模量 | 50.0mm跨距4 | ASTMD790 | 3840 | Mpa |
弯曲模量 | 100mmSpan5 | ASTMD790 | 3590 | Mpa |
弯曲模量 | ISO178 | 4160 | Mpa | |
弯曲应力 | ISO178 | 122 | Mpa | |
弯曲强度 | 屈服,50.0mm跨距4 | ASTMD790 | 116 | Mpa |
弯曲强度 | Yield,100mmSpan5 | ASTMD790 | 108 | Mpa |