物性信息：
| 吸水率 | 0.05 | % | ASTM D-570 |
| 模具收缩率 | |||
| (3.2mm,flow) | 0.25 | % | |
| (1.57mm.flow) | 0.16 | % | |
| 比重 | 1.67 | ASTM D-792 |
| IZOD冲击强度 (-40℃) | 80 | J/m | ASTM D-256 |
| 弯曲强度 (23℃) | 200 | MPa | ASTM D-790 |
| IZOD冲击强度 (23℃) | 91 | J/m | ASTM D-256 |
| 无缺口冲击强度 (23℃) | 585 | J/m | ASTM D-4812 |
| IZOD无缺口冲击强度 (-40℃) | 535 | J/m | ASTM D-4812 |
| 介电常数 | ASTM D-150 | ||
| (10) | 3.7 | ||
| (10) | 3.8 | ||
| 介电强度 (1.6mm) | 25.0 | kv/mm | ASTM D-149 |
| 体积电阻率 | 10 | Ω.cm | ASTM D-257 |
| 抗电弧性 | 60-120 | S | ASTM D-495 |
| 介电强度 (3.2mm) | 18.0 | kv/mm | ASTM D-149 |
| 表面电阻率 | 10 | Ω | ASTM D-257 |
| 损耗因数 | ASTM D-150 | ||
| (10) | 0.018 | ||
| (10) | 0.011 | ||
| CTI |