| 模具收缩率 (3.2mm) | - | E-3 | ASTM D-955 |
| 比重 | - | ASTM D-792 | |
| 吸水率 | - | % | ASTM D-570 |
| 冲击强度缺口 (23℃) | 535 | J/m | ASTM D-256 |
| 拉伸强度(屈伏点) | 67 | Mpa | ASTM D-638 |
| 弯曲模量 | 2691 | Mpa | ASTM D-790 |
| 弯曲强度 | 103 | Mpa | ASTM D-790 |
| 拉伸率(断裂点) | 50 | % | ASTM D-638 |
| 拉伸模量 | - | Mpa | ASTM D-638 |
| 洛氏硬度 | - | R | ASTM D-785 |
| 表面电阻 | - | Ohm-cm | ASTM D-257 |
| 损耗因数 (1MHz) | - | ASTM D-150 | |
| 体积电阻 | - | Ohm-cm | ASTM D-257 |
| 介电常数 (1MHz) | - | ASTM D-150 |
| 阻燃性 | 1.5 | UL94 | UL-94 |
| 热变形温度 (1.8Mpa) | 86 | ℃ | ASTM D-648 |
| UL长期使用温度 (无冲击) | 75 | ℃ | UL-746B |
| 维卡软化点 | - | ℃ | ASTM D-525 |
| 热变形温度 (0.45Mpa) | - | ℃ | ASTM D-648 |
| 阻燃性 | V-0 | UL-94 | |
| 线膨胀系数 | - | 1/℃ | E831 |
| UL长期使用温度 (含冲击) | 65 | ℃ | UL-746B |