TPE美国杜邦 5556
物理性能额定值 (公制)额定值 (英制)测试方法密度1.03 g/cc0.0372 lb/in³
1.19 g/cc0.0430 lb/in³ISO 1183吸水率0.60 %
@Thickness 2.00 mm
0.60 %
@Thickness 0.0787 in
Sim. to ISO 62水分吸收0.200 %
0.200 %
Sim. to ISO 62饱和吸水率0.60 %0.60 %Immersion 24h; ASTM D570粘度81295cP
@Shear Rate 5000 1/s, Temperature 240 °C
81295 cP
@Shear Rate 5000 1/s, Temperature 464 °F
ISO 11403-1 -2
88320 cP
@Shear Rate 5000 1/s, Temperature 230 °C
88320 cP
@Shear Rate 5000 1/s, Temperature 446 °F
ISO 11403-1 -2
96440 cP
@Shear Rate 5000 1/s, Temperature 220 °C
96440 cP
@Shear Rate 5000 1/s, Temperature 428 °F
ISO 11403-1 -2
321800 cP
@Shear Rate 500 1/s, Temperature 240 °C
321800 cP
@Shear Rate 500 1/s, Temperature 464 °F
ISO 11403-1 -2
358400 cP
@Shear Rate 500 1/s, Temperature 230 °C
358400 cP
@Shear Rate 500 1/s, Temperature 446 °F
ISO 11403-1 -2
400200 cP
@Shear Rate 500 1/s, Temperature 220 °C
400200 cP
@Shear Rate 500 1/s, Temperature 428 °F
ISO 11403-1 -2线性成型收缩率,Flow0.014 cm/cm0.014 in/inISO 294-42577线性成型收缩率,横向0.014 cm/cm0.014 in/inISO 294-4 2577熔体流动速率7.0 g/10min
@Load 2.16 kg, Temperature 220 °C
7.0 g/10 min
@Load 4.76 lb, Temperature 428 °F
cm³/10min; ISO 1133
7.8 g/10 min
7.8 g/10 min
ISO 1133机械性能额定值 (公制)额定值 (英制)测试方法肖氏硬度 (邵氏 D)515115s; ISO 868