PCTGDN003美国伊士曼 高韧性包装奶瓶原材料

手机版链接：https://m.trustexporter.com/cz12472590.htm
PCTGDN003美国伊士曼物性表物理性能测试条件测试方法测试结果单位密度 / 比重ASTMD7921.23g/cm³23°CISO11831.23g/cm³收缩率MD：3.20mmASTMD9550.20to0.50%吸水率23°C,24hrASTMD5700.13%23°C,24hrISO620.13%机械性能测试条件测试方法测试结果单位抗张强度屈服,23°CASTMD63845.0Mpa拉伸强度Yield,23°C,4.00mmISO527-246.0Mpa抗张强度断裂,23°CASTMD63852.0Mpa拉伸强度Break,23°C,4.00mmISO527-247.0Mpa伸长率屈服,23°CASTMD6385.0%TensileStrainYield,23°C,4.00mmISO527-24.4%伸长率断裂,23°CASTMD638330%TensileStrainBreak,23°C,4.00mmISO527-2230%弯曲模量23°CASTMD7901800Mpa23°C,4.00mmISO1781800Mpa弯曲强度23°C,4.00mmISO17863.0Mpa屈服,23°CASTMD79066.0Mpa热性能测试条件测试方法测试结果单位热变形温度0.45MPa,未退火ASTMD64874.0°C0.45MPa,未退火ISO75-2/B74.0°C1.8MPa,未退火ASTMD64864.0°C1.8MPa,未退火ISO75-2/A65.0°C维卡软化温度ASTMD1525288.0°C--ISO306/A88.0°C--ISO306/B79.0°C比热60°CDSC1340J/kg/°C240°CDSC2050J/kg/°C导热系数(23°C)DSC0.19W/m/K耐热性：PCTG可以在高温下进行热灌装，灌装后无需进行二次加热或冷却，减少了能源消耗和 生产成本。