日本东丽PBT（日本东丽 1184G-15）

手机版链接：https://m.trustexporter.com/cz12436214.htm
日本东丽1184G-15物性表物性性能测试条件测试方法测试结果单位密度ASTM D792/ISO 11831.56吸水率 23℃/24HASTM D570/ISO 620.07%物理性能测试条件测试方法测试结果单位吸水率23℃,24hrASTM D5700.07%机械性能测试条件测试方法测试结果单位拉伸强度23℃ASTM D638110Mpa伸长率23℃ASTM D6385%弯曲强度23℃ASTM D790150Mpa弯曲模量23℃ASTM D7905.6GPaIZOD缺口冲击强度缺口，23℃ASTM D25660J/m无缺口，23℃ASTM D25650KJ/m洛氏硬度ASTM D78587M摩擦系数-，对金属ASTM D18940.15-，对本身ASTM D18940.20断裂伸长率ASTM D638/ISO 5275%拉伸强度ASTM D638/ISO 527110kg/cm²(MPa)[Lb/in²]洛氏硬度ASTM D785M87弯曲模量ASTM D790/ISO 1785600kg/cm²(MPa)[Lb/in²]弯曲强度ASTM D790/ISO 178150kg/cm²(MPa)[Lb/in²]IZOD 缺口冲击强度ASTM D256/ISO 17960kg·cm/cm(J/M)ft·lb/inASTM D256/ISO 17950kg·cm/cm(J/M)ft·lb/in热性能测试条件测试方法测试结果单位热变形温度-，0.45MPaASTM D648215°C-，1.82MpaASTM D648200°C线膨胀系数ASTM D6965.3阻燃性UL94V-0燃烧性（率）UL94V-0热变形温度ASTM D648/ISO 75200℃（℉）线性膨胀系数ASTM D696/ISO 113595.3x10^-5mm/mm.℃电气性能测试条件测试方法测试结果单位介电常数ASTM D150/IEC 602503.8体积电阻率ASTM D257/IEC 600933.0x10^14Ω.cmASTM D2573.0耐电压ASTM D14925MV/m介电常数-，50HzASTM D1503.6-，10ASTM D1503.8介电损耗正切值-，50HzASTM D1500.002-，10ASTM D1500.02电弧电阻系数ASTM D495133S