Xenoy PC/PBT IQ1103 美国GE 耐低温抗撞击 汽车配件

手机版链接：https://m.trustexporter.com/cz13016147.htm
供应Xenoy PC/PBT IQ1103 美国GE 耐低温抗撞击 汽车配件SABIC Innovative Plastics Xenoy® IQ1103 PBT+PC 物性表物理性能额定值 (公制)额定值 (英制)测试方法比重1.19 g/cc1.19 g/ccASTM D792密度1.20 g/cc0.0434 lb/in³ISO 1183水分吸收0.0800 %0.0800 %23°C / 50% RH; ISO 62饱和吸水率0.30 %0.30 %ISO 62线性成型收缩率,Flow0.0080 - 0.012 cm/cm@Thickness 3.20 mm0.0080 - 0.012 in/in@Thickness 0.126 inSABIC Method熔体流动速率13 g/10 min@Load 5.00 kg, Temperature 250 °C13 g/10 min@Load 11.0 lb, Temperature 482 °FASTM D1238化合物熔体指数12 g/10 min@Load 5.00 kg, Temperature 250 °C12 g/10 min@Load 11.0 lb, Temperature 482 °FMVR [cm^3/10 min]; ISO 1133机械性能额定值 (公制)额定值 (英制)测试方法抗张强度(断裂)46.0 MPa6670 psiType I, 50 mm/min; ASTM D63847.0 MPa6820 psi50 mm/min; ISO 527抗张强度(屈服)45.0 MPa6530 psiType I, 50 mm/min; ASTM D63849.0 MPa7110 psi50 mm/min; ISO 527伸长率 (断裂)140 %140 %Type I, 50 mm/min; ASTM D638150 %150 %50 mm/min; ISO 527屈服伸长率4.0 %4.0 %Type I, 50 mm/min; ASTM D6384.0 %4.0 %50 mm/min; ISO 527拉伸模量1.95 GPa283 ksi1 mm/min; ISO 5272.05 GPa297 ksi50 mm/min; ASTM D638弯曲强度70.0 MPa10200 psi2 mm/min; ISO 17874.0 MPa10700 psi1.3 mm/min, 50 mm span; ASTM D790弯曲模量1.92 GPa278 ksi2 mm/min; ISO 1782.00 GPa290 ksi1.3 mm/min, 50 mm span; ASTM D790悬壁梁缺口冲击强度6.50 J/cm12.2 ft-lb/inASTM D2566.00 J/cm@Temperature -30.0 °C11.2 ft-lb/in@Temperature -22.0 °FASTM D25655.0 kJ/m²26.2 ft-lb/in²80*10*4; ISO 180/1A47.0 kJ/m²@Temperature -30.0 °C22.4 ft-lb/in²@Temperature -22.0 °F80*10*4; ISO 180/1A简支梁缺口冲击强度5.50 J/cm²26.2 ft-lb/in²Edgew 80*10*4 sp=62mm; ISO 179/1eA落锤总能量50.0 J@Temperature 23.0 °C36.9 ft-lb@Temperature 73.4 °FASTM D3763热性能额定值 (公制)额定值 (英制)测试方法线形热膨胀系数 - 流动90.0 µm/m-°C@Temperature -40.0 - 150 °C50.0 µin/in-°F@Temperature -40.0 - 302 °FASTM E 83190.0 µm/m-°C@Temperature -30.0 - 80.0 °C50.0 µin/in-°F@Temperature -22.0 - 176 °FISO 11359-2线性热膨胀系数,横向流动95.0 µm/m-°C@Temperature -40.0 - 150 °C52.8 µin/in-°F@Temperature -40.0 - 302 °FASTM E 83195.0 µm/m-°C@Temperature -30.0 - 80.0 °C52.8 µin/in-°F@Temperature -22.0 - 176 °FISO 11359-2载荷下热变形温度(0.46 MPa)99.0 °C@Thickness 3.20 mm210 °F@Thickness 0.126 inunannealed; ASTM D648载荷下热变形温度(1.8 MPa)76.0 °C169 °FFlatw 80*10*4 sp=64mm; ISO 75/Af75.0 °C@Thickness 3.20 mm167 °F@Thickness 0.126 inunannealed; ASTM D648维卡软化温度115 °C239 °FRate B/50; ISO 306117 °C243 °FRate B/120; ISO 306117 °C243 °FRate B/50; ASTM D1525