韩国ABS XR-407D 韩国LGXR-407D耐热级

手机版链接：https://m.trustexporter.com/cz12746073.htm
LG Chemical XR407D ABS 物性表物理性能额定值 (公制)额定值 (英制)测试方法比重1.07 g/cc1.07 g/ccASTM D792处理0.0100.010Injection Molding线性成型收缩率,Flow0.0040 - 0.0070 cm/cm@Thickness 3.20 mm0.0040 - 0.0070 in/in@Thickness 0.126 inASTM D955熔体流动速率6.0 g/10 min@Load 10.0 kg, Temperature 220 °C6.0 g/10 min@Load 22.0 lb, Temperature 428 °FASTM D1238机械性能额定值 (公制)额定值 (英制)测试方法洛氏硬度（R 级）111111ASTM D785抗张强度(屈服)47.1 MPa@Thickness 3.20 mm6830 psi@Thickness 0.126 in50 mm/min; ASTM D638伸长率 (断裂)20 %@Thickness 3.20 mm20 %@Thickness 0.126 in50 mm/min; ASTM D638弯曲强度77.5 MPa@Thickness 3.20 mm11200 psi@Thickness 0.126 in15 mm/min; ASTM D790弯曲模量2.45 GPa@Thickness 3.20 mm356 ksi@Thickness 0.126 in15 mm/min; ASTM D790悬壁梁缺口冲击强度1.57 J/cm@Thickness 6.40 mm, Temperature 23.0 °C2.94 ft-lb/in@Thickness 0.252 in, Temperature 73.4 °FASTM D2561.67 J/cm@Thickness 3.20 mm, Temperature 23.0 °C3.12 ft-lb/in@Thickness 0.126 in, Temperature 73.4 °FASTM D256Izod Impact, Unnotched0.785 J/cm@Thickness 6.40 mm, Temperature -30.0 °C1.47 ft-lb/in@Thickness 0.252 in, Temperature -22.0 °FASTM D2560.785 J/cm@Thickness 3.20 mm, Temperature -30.0 °C1.47 ft-lb/in@Thickness 0.126 in, Temperature -22.0 °FASTM D256热性能额定值 (公制)额定值 (英制)测试方法载荷下热变形温度(0.46 MPa)113 °C@Thickness 6.40 mm235 °F@Thickness 0.252 inUnannealed; ASTM D648载荷下热变形温度(1.8 MPa)104 °C@Thickness 6.40 mm219 °F@Thickness 0.252 inUnannealed; ASTM D648维卡软化温度111 °C@Load 5.00 kg232 °F@Load 11.0 lb50°C/h; ASTM D1525UL RTI60.0 °C@Thickness >=1.50 mm140 °F@Thickness >=0.0591 inUL 746B60.0 °C@Thickness >=3.00 mm140 °F@Thickness >=0.118 inUL 746BUL RTI，机械冲击60.0 °C@Thickness >=1.50 mmUL 746BUL RTI，机械无冲击60.0 °C@Thickness >=1.50 mmUL 746B可燃性(UL94)HB@Thickness >=1.50 mmHB@Thickness >=0.0591 inHB@Thickness >=3.00 mmHB@Thickness >=0.118 in加工性能额定值 (公制)额定值 (英制)测试方法料筒后部温度180 - 220 °C356 - 428 °FInjection Molding料筒中部温度220 - 240 °C428 - 464 °FInjection Molding料筒前部温度230 - 250 °C446 - 482 °FInjection Molding射嘴温度240 - 250 °C464 - 482 °FInjection Molding加工（熔体）温度230 - 250 °C446 - 482 °FInjection Molding模具温度60.0 - 80.0 °C140 - 176 °FInjection Molding干燥温度80.0 - 90.0 °C176 - 194 °FInjection Molding干燥时间3.00 - 4.00 hour3.00 - 4.00 hourInjection Molding背压1.96 - 3.92 MPa284 - 569 psiInjection Molding螺杆转速50 - 100 rpm50 - 100 rpmInjection Molding