SABIC Innovative Plastics Cycolac® G366 ABS (Europe-Africa-Middle East) 物性表物理性能额定值 (公制)额定值 (英制)测试方法密度1.05 g/cc0.0379 lb/in³ISO 1183平衡吸湿0.20 %0.20 %23°C / 50% RH; ISO 62饱和吸水率1.0 %@Temperature 23.0 °C1.0 %@Temperature 73.4 °FISO 62线性成型收缩率,Flow0.0050 - 0.0070 cm/cm0.0050 - 0.0070 in/inon tensile bar; SABIC Method熔体流动速率8.0 g/10 min@Load 10.0 kg, Temperature 220 °C8.0 g/10 min@Load 22.0 lb, Temperature 428 °FISO 11338.0 g/10 min@Load 10.0 kg, Temperature 220 °C[cm^3/10 min] Melt Volume Rate; ISO 1133机械性能额定值 (公制)额定值 (英制)测试方法洛氏硬度(R 级)115115ISO 2039-2硬度,H358/3099.0 MPa14400 psiISO 2039-1抗张强度(断裂)30.0 MPa4350 psi5 mm/min; ISO 52740.0 MPa5800 psi50 mm/min; ISO 527抗张强度(屈服)45.0 MPa6530 psi5 mm/min; ISO 52750.0 MPa7250 psi50 mm/min; ISO 527伸长率 (断裂)15 %15 %5 mm/min; ISO 52715 %15 %50 mm/min; ISO 527屈服伸长率2.0 %2.0 %5 mm/min; ISO 5273.0 %3.0 %50 mm/min; ISO 527拉伸模量2.60 GPa377 ksi1 mm/min; ISO 527弯曲强度74.0 MPa10700 psi2 mm/min; ISO 178弯曲模量2.60 GPa377 ksi2 mm/min; ISO 178悬壁梁缺口冲击强度6.00 kJ/m²@Temperature -30.0 °C2.86 ft-lb/in²@Temperature -22.0 °F80*10*4; ISO 180/1A12.0 kJ/m²@Temperature 23.0 °C5.71 ft-lb/in²@Temperature 73.4 °F80*10*4; ISO 180/1A简支梁缺口冲击强度0.700 J/cm²@Temperature -30.0 °C3.33 ft-lb/in²@Temperature -22.0 °FV-notch Edgew 80*10*4 sp=62mm; ISO 179/1eA1.20 J/cm²@Temperature 23.0 °CV-notch Edgew 80*10*4 sp=62mm; ISO 179/1eA泰伯磨损,毫克/1000次100@Load 1.00 kg100@Load 2.20 lbCS-17; SABIC Method电气性能额定值 (公制)额定值 (英制)测试方法体积电阻率>= 1.00e+15 ohm-cm>= 1.00e+15 ohm-cmIEC 60093表面电阻>= 1.00e+15 ohm>= 1.00e+15 ohmROA; IEC 60093介电常数2.8@Frequency 1.00e+6 Hz2.8@Frequency 1.00e+6 HzIEC 602502.9@Frequency 50.0 - 60.0 Hz2.9@Frequency 50.0 - 60.0 HzIEC 60250介电强度18.0 kV/mm@Thickness 3.20 mm457 kV/in@Thickness 0.126 inin oil; IEC 60243-126.0 kV/mm@Thickness 1.60 mm660 kV/in@Thickness 0.0630 inin oil; IEC 60243-135.0 kV/mm@Thickness 0.800 mm889 kV/in@Thickness 0.0315 inin oil; IEC 60243-1耗散因数0.011@Frequency 50.0 - 60.0 Hz0.011@Frequency 50.0 - 60.0 HzIEC 602500.014@Frequency 1.00e+6 Hz0.014@Frequency 1.00e+6 HzIEC 60250相比耐漏电起痕指数(CTI)575 V575 VIEC 60112热性能额定值 (公制)额定值 (英制)测试方法线形热膨胀系数 - 流动80.0 µm/m-°C@Temperature 23.0 - 60.0 °C44.4 µin/in-°F@Temperature 73.4 - 140 °FISO 11359-2线性热膨胀系数,横向流动80.0 µm/m-°C@Temperature 23.0 - 60.0 °CISO 11359-2导热系数0.200 W/m-K1.39 BTU-in/hr-ft²-°FISO 8302载荷下热变形温度(0.46 MPa)96.0 °C205 °FEdgew 120*10*4 sp=100mm; ISO 75/Be载荷下热变形温度(1.8 MPa)82.0 °C180 °FEdgew 120*10*4 sp=100mm; ISO 75/Ae维卡软化温度106 °C223 °FRate B/50; ISO 306108 °C226 °FRate B/120; ISO 306UL RTI80.0 °C176 °FUL 746BUL RTI,机械冲击80.0 °C176 °FUL 746BUL RTI,机械无冲击80.0 °C176 °FUL 746B可燃性(UL94)HB@Thickness 1.50 mmHB@Thickness 0.0591 inUL 94HB@Thickness 3.00 mmHB@Thickness 0.118 in2nd value; UL 94Flame Spread25.0 mm/min@Thickness 1.00 mm0.984 in/min@Thickness 0.0394 inFMVSS 302灼热丝易燃指数650 °C@Thickness 3.20 mm1200 °F@Thickness 0.126 inGlow Wire Flammability Index; IEC 60695-2-12750 °C@Thickness 1.00 mm1380 °F@Thickness 0.0394 inGlow Wire Flammability Index; IEC 60695-2-12