供应PA6日本东丽CM1011G-45 增强级 高流动 聚酰胺尼龙6详细介绍Amilan® CM1011G-45是一种聚酰胺6（尼龙6）产品,含有的填充物为45% 玻璃纤维增强材料。 它,在北美洲、欧洲或亚太地区有供货。 主要特性为:阻燃/额定火焰。PA6日本东丽CM1011G-45物性表原料技术数据性能项目试验条件[状态]测试方法测试数据数据单位基本性能吸水率23℃，24hrASTM D-570Dry｜1.9%Water0.9｜-%吸水率23℃ASTM D-570Dry｜1.9%Water5.3｜-%物理性能比重ASTM D-792Dry｜1.9%Water1.50｜-机械性能断裂伸长率-40℃ASTM D-638Dry｜1.9%Water4.5｜4.5%弯曲模量23℃ASTM D-790Dry｜1.9%Water12.0｜7.1GPaIZOD缺口冲击强度-40℃ASTM D-256Dry｜1.9%Water125｜145J/m弯曲模量80℃ASTM D-790Dry｜1.9%Water6.2｜4.4GPa拉伸屈服强度23℃ASTM D-638Dry｜1.9%Water205｜130MPa弯曲模量-40℃ASTM D-790Dry｜1.9%Water14.0｜12.5GPa弯曲强度23℃ASTM D-790Dry｜1.9%Water290｜180MPa断裂伸长率23℃ASTM D-638Dry｜1.9%Water5.0｜5.0%拉伸屈服强度80℃ASTM D-638Dry｜1.9%Water120｜85MPaIZOD无缺口冲击强度23℃ASTM D-256Dry｜1.9%Water100｜120KJ/m2弯曲强度-40℃ASTM D-790Dry｜1.9%Water330｜280MPaIZOD缺口冲击强度23℃ASTM D-256Dry｜1.9%Water155｜195J/m抗压强度-40℃ASTM D-695Dry｜1.9%Water260｜220MPa抗压强度23℃ASTM D-695Dry｜1.9%Water190｜120MPa抗压强度80℃ASTM D-695Dry｜1.9%Water100｜70MPa剪切强度23℃ASTM D-732Dry｜1.9%Water95｜75MPa断裂伸长率80℃ASTM D-638Dry｜1.9%Water8.0｜8.0%弯曲强度80℃ASTM D-790Dry｜1.9%Water160｜110MPa洛氏硬度23℃ASTM D-785Dry｜1.9%WaterR121,M95｜-R ScaleIZOD无缺口冲击强度-40℃ASTM D-256Dry｜1.9%Water90｜95KJ/m2拉伸屈服强度-40℃ASTM D-638Dry｜1.9%Water290｜250MPa热性能热导率Dry｜1.9%Water0.40｜-W/m℃线性热膨胀系数ASTM D-696Dry｜1.9%Water2-3｜-10-5/℃比热Dry｜1.9%Water1.4｜-J/p℃熔点DSCDry｜1.9%Water225｜-℃热变形温度0.46MPaASTM D-648Dry｜1.9%Water225｜-℃热变形温度1.86MPaASTM D-648Dry｜1.9%Water215｜-℃其它性能加强材料Dry｜1.9%Water45｜45WT%优良的耐化学品性吸水率低　　对于尼龙树脂而言，PA6T的吸水率相当低，仅为尼龙66的1/4至1/3。因此，PA6T因吸水所造成的物性变化相对较小。优良的尺寸稳定性　　PA6T的吸水率相当低，因吸水而造成的尺寸变化相当小。 PA6T的热膨胀系数相当稳定，在高温范围中仍然维持在相当低的水准，因此，对温度变化的尺寸稳定性良好。 此外，PA6T因成型过程所造成翘曲很小。也就是说PA6T具有优良的尺寸稳定性。