MULTILON PC/ABS TN-7000---产品说明:Halogen-free flame retardant PC/ABS polymer alloy, and is also antimony-free. It is a typical type with high flowability, light resistance and heat stability that is suitable for a business machine chassis etc..
Information provided by Teijin Chemicals Ltd.
无卤阻燃PC/ABS聚合物合金,也不含锑。它是一种典型的高流动性、耐光性和热稳定性的类型,适用于商业机器底盘等。。
帝人化学有限公司提供的信息。
PC/ABS TN-7000物性信息:
密度 | 1.18 g/cc | 0.0426 lb/in³ | ISO 1183 |
线性成型收缩率 | 0.0040 - 0.0060 cm/cm @Thickness 4.00 mm | 0.0040 - 0.0060 in/in @Thickness 0.157 in | |
线性成型收缩率,横向 | 0.0040 - 0.0060 cm/cm @Thickness 4.00 mm |
抗张强度(断裂) | 48.0 MPa | 6960 psi | 50mm/min; ISO 527 |
抗张强度(屈服) | 63.0 MPa | 9140 psi | 50mm/min; ISO 527 |
伸长率 (断裂) | 80 % | 80 % | 50mm/min; ISO 527 |
屈服伸长率 | 3.0 % | 3.0 % | 50mm/min; ISO 527 |
弯曲强度 | 95.0 MPa | 13800 psi | 2mm/min; ISO 178 |
弯曲模量 | 2.60 GPa | 377 ksi | 2mm/min; ISO 178 |
简支梁无缺口冲击强度 | NB | NB | ISO 179 |
简支梁缺口冲击强度 | 1.50 J/cm² | 7.14 ft-lb/in² | ISO 179 |