| 密度 | 1.78 g/cc | 0.0643 lb/in³ | ISO 1183 |
| 吸水率 | = 1.00e+14 ohm-cm | Intensity = 10 mA after 2 min @ 23°C; ASTM D 257; DIN 53483 | |
| 表面电阻 | >= 1.00e+14 ohm | >= 1.00e+14 ohm | Voltage < 1 V after 2 min - 500 V; ASTM D 257/DIN 53483 |
| Heat of Fusion | 59.0 J/g | 25.4 BTU/lb | Crystallization Heat |
| 67.0 J/g | 28.8 BTU/lb | 80°C to end of melting | |
| 线性热膨胀系数 | 120 - 140 µm/m-°C @Temperature 20.0 °C | 66.7 - 77.8 µin/in-°F @Temperature 68.0 °F | ASTM D696 |
| 比热容 | 1.20 J/g-°C | 0.287 BTU/lb-°F | |
| 1.60 J/g-°C @Temperature 100 °C | 0.382 BTU/lb-°F @Temperature 212 °F | ||
| 导热系数 | 0.200 W/m-K | 1.39 BTU-in/hr-ft²-°F | ASTM C177 |
| 熔融温度 | 174 °C | 345 °F | Crystallinity by DSC; ASTM D 3418 |
| Crystallization Temperature | 140 °C | 284 °F | |
| 载荷下热变形温度(0.46 MPa) | 148 °C @Thickness 4.00 mm | 298 °F @Thickness 0.157 in | after annealing 150°C 16 hr; ASTM D648 |
| 载荷下热变形温度(1.8 MPa) | 115 °C @Thickness 4.00 mm | 239 °F @Thickness 0.157 in | after annealing 150°C 16 hr; ASTM D648 |
| 维卡软化温度 | 171 °C @Load 1.00 kg, Thickness 4.00 mm | 340 °F @Load 2.20 lb, Thickness 0.157 in | ISO 306 |
| 脆化温度 | 0.000 - 10.0 °C | 32.0 - 50.0 °F | ASTM D746A |
| 玻璃化转变温度，Tg | -30.0 °C | -22.0 °F | DMTA |
| 分解温度 | 375 - 400 °C | 707 - 752 °F | Thermal Stability via TGA : beginning - and at 1% weight loss in air |
| 可燃性(UL94) | V-0 | V-0 | |
| 极限氧指数 | 44 % @Thickness 3.00 mm | 44 % @Thickness 0.118 in | sheet; ASTM D2863 |