导热矿物填充尼龙6 LNP Konduit PX09322

导热矿物填充尼龙6 LNP Konduit PX09322
PA6 美国液氮 PX09322
SABIC Innovative Plastics LNP KONDUIT PX09322 PA 6
LNP Konduit PX09322 白颜色的导热矿物填充尼龙6，阻燃FR化合物。
热性能：
CTE, linear, Parallel to Flow 23.7 µm/m-°C
@Temperature -40.0 - 40.0 °C 13.2 µin/in-°F
@Temperature -40.0 - 104 °F ASTM E 831
CTE, linear, Transverse to Flow 36.7 µm/m-°C
@Temperature -40.0 - 40.0 °C 20.4 µin/in-°F
@Temperature -40.0 - 104 °F ASTM E 831
Thermal Conductivity 0.860 W/m-K 5.97 BTU-in/hr-ft²-°F through-plane, ø80*3mm discs; ISO 22007-2
1.50 W/m-K 10.4 BTU-in/hr-ft²-°F through-plane, 10*10*3mm sample; ASTM E 1461-07
2.68 W/m-K 18.6 BTU-in/hr-ft²-°F in-plane, ø80*3mm discs; ISO 22007-2
6.00 W/m-K 41.6 BTU-in/hr-ft²-°F in-plane, ø25*0.4mm disc; ASTM E 1461-07
Deflection Temperature at 0.46 MPa (66 psi) 210 °C
@Thickness 6.40 mm 410 °F
@Thickness 0.252 in unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 182 °C
@Thickness 6.40 mm 360 °F
@Thickness 0.252 in unannealed; ASTM D648
Flammability, UL94 V-0
@Thickness 1.20 mm V-0
@Thickness 0.0472 in UL 94
Glow Wire Test 960 °C
@Thickness 1.00 mm 1760 °F
@Thickness 0.0394 in IEC 60695-2-12